Thermal shock resistant low creep high-aluminum series for hot blast furnaces
The series of products represent the improvement of low creep brick products, in addition to a low creep rate, more notable features include high thermal shock stability, in 2003, it passed the results appraisal organized by Henan Metallurgy Department, and successively supplied over 5,000 tons of hot blast furnace for Baosteel and TISCO, and the indexes have reached or even exceeded the level of the similar products introduced by Baosteel from Japan. In 2004, it was awarded the Metallurgical Science and Technology Award by the China Iron and Steel Association.
Index |
WH21 |
WH 22 |
WH 23 |
WH 231 |
WH 24 |
WH 25 |
WHIMF |
WML-72 |
Al2O3 % |
≥75 |
≥80 |
≥65 |
≥65 |
≥65 |
≥65 |
≥70 |
≥72 |
Fe2O3 % |
≤1.0 |
≤1.0 |
≤1.2 |
≤1.2 |
≤1.5 |
≤1.8 |
≤1.5 |
≤1.0 |
Apparent porosity % |
≤21 |
≤21 |
≤21 |
≤20 |
≤22 |
≤22 |
≤22 |
≤24 |
Bulk density BD ,g/cm3 |
≥2.70 |
≥2.75 |
≥2.60 |
≥2.60 |
≥2.50 |
≥2.45 |
≥2.5 |
≥2.70 |
Normal temperature compressive strength CSS, MPa |
≥70 |
≥70 |
≥65 |
≥65 |
≥60 |
≥60 |
≥60 |
≥50 |
Softening onset temperature at 0.2 MPa load RUL,℃ |
≥1700 |
≥1700 |
≥1650 |
≥1650 |
≥1600 |
≥1550 |
≥1600 |
≥1550 |
Reburning line change rate PLC(%) |
1500℃×4h |
1500℃×4h |
1500℃×4h |
1450℃×3h |
1450℃×3h |
1450℃×3h |
1500℃×4h |
1500℃×4h |
Creep rate(0.2MPa),% |
1550℃×50h≤0.8 |
1500℃×50h≤0.8 |
1450℃×50h≤0.8 |
1450℃×50h≤0.8 |
1400℃×50h≤0.8 |
1350℃×50h≤0.8 |
/ |
1500℃×50h≤0.8 |
TSR ,(1100℃water cooling)次Cycle |
≥15 |
≥15 |
≥15 |
≥30 |
≥15 |
≥15 |
≥25 |
≥40 |
Note: Thermal shock stability index is adjustable as per the requirements of customers |
Relevant case
If you are interested in related products, welcome to leave us a message ~
Henan Winna Group Industries Co., Ltd.
Service Hotline:
Address:
Beishankou Town, Gongyi, Henan Province
Copyright©Henan Winna Group Industries Co., Ltd. 豫ICP备2023013320号 Powered by www.300.cn This website already supports IPv6